      Toughness and durability

    •  Good processability

    •  Good blending characteristics with HDPE HMW resins

    Typical applications for HHM TR-144 include:

    •  T-shirt bags

    •  Multi-wall liners

      Trash bags

    This resin meets these specifications:

     FDA 21 CFR 177.1520(c) 3.2a

     EU No. 10/2011

    For a Material Safety Data Sheet (MSDS), visit our site at www.saudipolymers.com

    Nominal Resin Properties Value (SI Units) Method
    Density 0.946 g/cm3 ASTM D1505
    Melt Index, Condition 190°C / 2.16 kg 0.18 g/10 min  ASTM D1238
    Brittleness Temperature, Type A clamp, Type I specimen <-75°C ASTM D746
    ESCR, Condition B (100% Igepal), F50 >1000 hrs ASTM D1693
    Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min 1150 MPa ASTM D790
    Dart Drop (66 cm) 90 g ASTM D1709
    Tensile Strength at Yield, 50.8 mm/min MD 24 MPa ASTM D882
    Tensile Strength at Yield, 50.8 mm/min TD 26 MPa ASTM D882
    Elongation at Break, 50.8 mm/min MD 480% ASTM D882
    Elongation at Break, 50.8 mm/min TD 640%  ASTM D882
    Elmendorf Tear Strength, MD 19 g ASTM D1922
    Elmendorf Tear Strength, TD 270 g ASTM D1922


    1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should not be used for specification purposes. Values are rounded.

    2. The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM D4703, Annex A1.

    3. Based on 0.025 mm film produced at 4:1 blow-up ratio.