The LD 165 series are LDPE grades, offering high strength combined with medium optical properties.
Applications
Widely used in Agricultural Film, Foams, Pallet shrink Film, Blend Partner, Heavy Duty Bags, Blend Partner, Construction Film, High Performance CollationShrink
Resin Properties
Typical Value (English)
Typical Value (SI)
Test Based On
Density
0.922 g/cm³
0.922 g/cm³
A5TMD1505
Melt Index2 (190*C/2.16 kg)
0.33 g/10 min
0.33 g/10 min
ASTMD1238
Peak Melting Temperature
229℉
109℃
ExxonMobilMethod
Film Properties
Typical Value (English)
Typical Value (SI)
Test Based On
Tensile Strength at Yield MD
1800 psi
13 MPa
ASTM D882
Tensile Strength at Yield TD
1700 psi
12 MPa
ASTM D882
Tensile Strength at Break MD
2900 psi
20 MPa
ASTM D882
Tensile Strength at Break TD
2500 psi
18 MPa
ASTM D882
Elongation at Break MD
280 %
280 %
ASTM D882
Elongation at Break TD
540 %
540 %
ASTM D882
Secant Modulus MD - 1% Secant
33000 psi
230 MPa
ASTM D882
Secant Modulus TD - 1% Secant
41000 psi
280 MPa
ASTM D882
Dart Drop Impact
490g
490g
ASTM D1709A
Elmendorf Tear Strength MD
260g
260g
ASTM D1922
Elmendorf Tear Strength TD
460g
460g
ASTM D1922
Legal Statement
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance e.q. FDA,EU,HPFB. This product is not intended for use in medical applications and should not be used in any such applications.
Processina Statement
The test specimen were prepared on LD 165BW1, 150um (5.9 mi) thick flm, using a 200 mm (7.9 in) die, die gap of 1.0 mm (39.4 mi), Blow-UpRatio of 1.5 and temperature profile of 145 - 190℃ (293 - 374℉).
Notes
Typical properties: these are not to be construed as specifications. 1.Product may not be available in one or ore countries in the identifed Avalability regions. Please contact your Sales Representative for complete Country Availability. 2. Value reported is an estimate based on ExxonMobi's correlation from melt flow rate data measured at other standard conditions, based on ASTM. D 1238