HTA 108 is a homopolymer HDPE film grade designed to improve stiffness and barrier in coextrusion or in PE blends. Whenblended with LLDPE or metallocene LLDPE, HTA 108 improves their processability.
Applications
Blown Film、Bread Bags、Colllation Shrink、Food Packagin、 Form Filll And Seall Packagiing、Freezer Fillm...
Resin Properties
Typical Value (English)
Typical Value (SI)
Test Based On
Density
0.961 g/cm³
0.961 g/cm³
A5TMD1505
Melt Index2 (190*C/2.16 kg)
0.70 g/10 min
0.70 g/10 min
ASTMD1238
High Load Melt Index (190℃/21.6 kg)
46 g/10 min
46 g/10 min
ASTMD1238
Film Properties
Typical Value (English)
Typical Value (SI)
Test Based On
Tensile Strength at Break MD
8700 psi
60 MPa
ASTM D882
Tensile Strength at Break TD
4500 psi
31 MPa
ASTM D882
Elongation at Break MD
510 %
510 %
ASTM D882
Elongation at Break TD
2 %
2 %
ASTM D882
Secant Modulus MD - 1% Secant
17000 psi
1200 MPa
ASTM D882
Secant Modulus TD - 1% Secant
25000 psi
1700 MPa
ASTM D882
Dart Drop Impact
<30g
<30g
ASTM D1709A
Elmendorf Tear Strength MD
10g
10g
ASTM D1922
Elmendorf Tear Strength TD
200g
200g
ASTM D1922
Legal Statement
Contact your ExxonMobil Chemical Customer Service Representative for potential food contact application compliance (e.g. FDA, EL, HPFB).
This product is not intended for use in medical applications and should not be used in any suchapplications.
Processina Statement
The test specimens for Vicat Softeniing Point were prepared using ASTM D 4703. All fillm properties have been measured on 25 pm (0.98 mill) thick fillms (BUR of2.5: 1, pocket extrusion at 200℃ / 392'F). Properties of coextruded films and blends can be fo und in the HTA108 Fact Sheet.
Notes
Typicallproperties these are not to be construed as specifications. 1 Product may not be availlable in one or more countries in the identified Availlability regions. Please contact your Sales Representative for complete Country Availability.