No.
|
Resin Properties
|
Typical value
|
Unit
|
Test Method
|
|
1
|
Specific Gravity, 23℃ |
1.05 |
g/cm³ |
ASTM D792
|
|
2
|
Mold Shrinkage, 23℃, 3.2mm,23℃
|
0.4-0.7 |
% |
ASTM D955
|
|
3
|
Melt Flow Rate, 220℃, 10kg |
22
|
g/10min |
ASTM D1238
|
| 4 |
Tensile Strength at Yield, 23℃, 50mm/min, 3.2mm |
49
|
MPa |
ASTM D638 |
| 5 |
Tensile Elongation at Yield, 23℃, 50mm/min, 3.2mm |
5
|
%, (Min) |
ASTM D638 |
|
6
|
Tensile Elongation at Break, 23'℃, 50mm/min, 3.2mm |
10
|
%, (Min) |
ASTM D638 |
|
7
|
Tensile Modulus, 23℃, 50mm/min, 3.2mm |
2350
|
MPa |
ASTM D638 |
|
8
|
Flexural Strength, 23℃, 15mm/min, 3.2mm |
78
|
MPa |
ASTM D790 |
|
9
|
Flexural Modulus, 23℃, 15mm/min, 3.2mm |
2550
|
MPa |
ASTM D790 |
|
10
|
Izod Impact Strength, Notched, 3.2mm, 23℃ |
220
|
J/m |
ASTM D256 |
|
11
|
Izod Impact Strength, Notched, 3.2mm, -30℃ |
90
|
J/m |
ASTM D256 |
|
12
|
Izod Impact Strength, Notched, 6.4mm, 23℃ |
220
|
J/m |
ASTM D256 |
|
13
|
Izod Impact Strength, Notched, 6.4mm,-30℃ |
90
|
J/m |
ASTM D256 |
| 14 |
Rockwell Hardness, R-Scale |
110 |
/ |
ASTM D785 |
| 15 |
HDT, Edgewise, 1.82MPa, 6.4mm, Unannealed |
85 |
°C |
ASTM D648 |
| 16 |
VICAT, 50N, 50℃/h |
92 |
°C |
ASTM D1525 |
| 17 |
RTI Electrical |
95 |
°C |
UL 746B |
| 18 |
RTI Mechanical with Impact |
95 |
°C |
UL 746B |
| 19 |
RTI Mechanical without Impact |
95 |
°C |
UL 746B |
| 20 |
Flammability, 1.5mm |
HB |
/ |
UL 94 |
| 21 |
Flammability, 3.0mm |
HB |
/ |
UL 94 |