PA66 101L

Short Description:

101L is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength; good toughness; high impact; good surface lubricity; abrasion resistance; resistant low temperature; self-extinguishment.

Price: Negotiable USD/MT

Port: SHANGHAI,NINGBO
MOQ: 1Mt
Cas Number: 32131-17-2
HS Code: 3908101101
Payment: TT, LC

Send email to us Download as PDF

Product Detail

Features

Nature colour,Medium viscosity,General purpose

Applications

It is suitable for compounding and injection moulding, also widely used in spinning monofilament, staple. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances,communications, textile, oil pipe/tank and precision engineering products, etc., it also can be used for the production of film, packing, medical equipment, sporting goods, and daily necessities and so on.

Packaging

In 25kg/bag,26MT/40HQ with pallets

Property	Test Method	Test Conditions	Unit	Test Result
Grade	Zytel® 101L NC010
General Information
Resin Identification	ISO 1043	/	-	PA66
Part Marking Code	ISO 11469	/	-	PA66
Rheological Properties
Viscosity Number	ISO 307, 1157, 1628	Sulfuric Acid 96%	cm³/g	150
Moulding Shrinkage, Parallel	ISO 294-4, 2577	Dry	%	1.4
Moulding Shrinkage, Normal	ISO 294-4, 2577	Dry	%	1.4
Mechanical Properties
Tensile Modulus	ISO 527-1/-2	Dry / Conditioned	MPa	3100 / 1400
Yield Stress	ISO 527-1/-2	Dry / Conditioned	MPa	82 / 55
Yield Strain	ISO 527-1/-2	Dry / Conditioned	%	4.5 / 25
Nominal Strain at Break	ISO 527-1/-2	Dry / Conditioned	%	25 / >50
Strain at Break	ISO 527-1/-2	23℃, 50mm/min	%	45
Flexural Modulus	ISO 178	Dry / Conditioned	MPa	2800 / 1200
Charpy Notched Impact Strength	ISO 179/1eA	23℃, Dry / Conditioned	kJ/m²	5.5 / 15
Izod Notched Impact Strength	ISO 180/1A	23℃, Dry / Conditioned	kJ/m²	5.5 / 12
Ball Indentation Hardness	ISO 2039-1	H 358/30, Dry / Conditioned	MPa	180 / 85
Rockwell Hardness, M-Scale	ISO 2039-2	Dry / Conditioned	-	79 / 59
Rockwell Hardness, R-Scale	ISO 2039-2	Dry / Conditioned	-	121 / 108
Thermal Properties
Melting Temperature	ISO 11357-1/-3	10℃/min, Dry	℃	262
Glass Transition Temperature	ISO 11357-1/-2	10℃/min, Dry	℃	60
Heat Deflection Temperature	ISO 75-1/-2	1.8MPa	℃	70
Heat Deflection Temperature	ISO 75-1/-2	0.45MPa	℃	190
Vicat Softening Temperature	ISO 306	50℃/h, 50N	℃	240
Coefficient of Linear Thermal Expansion, Parallel	ISO 11359-1/-2	Dry	E-6/K	100
Coefficient of Linear Thermal Expansion, Normal	ISO 11359-1/-2	Dry	E-6/K	110
Flammability
Burning Behavior	IEC 60695-11-10 / UL 94	1.5mm nominal thickness	Class	V-2
Oxygen Index	ISO 4589-1/-2	Dry	%	28
Glow Wire Flammability Index	IEC 60695-2-12	0.75mm / 1.5mm / 3mm	℃	960 / 960 / 960
Glow Wire Ignition Temperature	IEC 60695-2-13	0.75mm / 1.5mm / 3mm	℃	725 / 750 / 800
Electrical Properties
Relative Permittivity	IEC 62631-2-1	100Hz, Dry / Conditioned	-	3.8 / 11
Relative Permittivity	IEC 62631-2-1	1MHz, Dry / Conditioned	-	3.5 / 4
Volume Resistivity	IEC 62631-3-1	Dry / Conditioned	Ω·m	1E12 / 1E10
Electric Strength	IEC 60243-1	Dry / Conditioned	kV/mm	32 / 28
Comparative Tracking Index	IEC 60112	Dry	-	600
Other Properties
Density	ISO 1183	Dry	kg/m³	1140
Humidity Absorption	Sim. to ISO 62	2mm	%	2.6
Water Absorption	Sim. to ISO 62	2mm	%	8.5
Water Absorption, Immersion	Sim. to ISO 62	24h, 1mm thickness	%	4.2
Injection Molding Conditions
Drying Recommended	/	Injection Moulding	-	Yes
Drying Temperature	/	Dehumidified Dryer	℃	≥80
Drying Time	/	Dehumidified Dryer	h	2–4
Processing Moisture Content	/	Before Processing	%	≤0.2
Melt Temperature	/	Optimum	℃	290
Melt Temperature Range	/	Minimum / Maximum	℃	280–300
Mold Temperature	/	Optimum	℃	70
Mold Temperature Range	/	Minimum / Maximum	℃	50–90
Hold Pressure Range	/	Injection Moulding	MPa	50–100
Hold Pressure Time	/	Injection Moulding	s/mm	4

Note:

Zytel® 101L NC010 is a lubricated polyamide 66 resin for injection moulding. Values are presented as Dry / Conditioned where both values are provided in the original TDS. This data should not be used alone to establish specification limits or as the sole basis of design.